IEC 62417:2010 pdf free download Semiconductor devices – Mobile ion tests for metal-oxide semiconductor field effect transistors (MOSFETs)
1 Scope
This present standard provides a wafer level test procedure to determine the amount of positive mobile charge in oxide layers in metal-oxide semiconductor field effect transistors. . It is applicable to both active and parasitic field effect transistors. The mobile charge can cause degradation of microelectronic devices, e.g. by shifting the threshold voltage of MOSFETs or by inversion of the base in bipolar transistors.
2Abbreviations and letter symbols
This standard uses the following abbreviations and letter symbols:cv test
capacitance-voltage measurement
HFCV test high frequency capacitance-voltage measurementvg
gate voltage
tox oxide thickness
ds drain-source current
Ved positive power supply voltage
Vad,max maximum supply voltage
v transistor threshold voltage
t,initialthe absolute value of the threshold voltage before the testVsupply
the absolute value of the supply voltage
Eox dielectric constant of the oxide
3General description
The stress applied is on test structures at an elevated temperature where mobile ions canovercome the energy barriers at the interfaces and the ion mobility in the oxide is sufficientlyhigh. Two test methods are described in this document.
Bias temperature stress (BTS)
voltage sweep (vs).
The bias temperature stress test is done on transistors. The threshold voltage is determinedfrom an lds -Vas measurement at room temperature on fresh structures.The threshold voltageis defined as the gate voltage needed to force a fixed drain current through the transistor.Then,a positive gate stress is applied at a high temperature,to sweep the mobile ionstowards the substrate.After the stress the test structure is cooled to room temperature withthe bias still applied. A second lds – Vas curve is measured at room temperature. Thesequence is completed with a negative gate stress at high temperature followed by an lds -‘measurement at room temperature.Mobile charge causes a shift in the lds – vgs curve.The distance over which the curve is shifted is a measure of the amount of mobile charge inthe insulator.
Edge effects of the transistor structure can be taken into account by applying a negative gate bias for 2 minutes duration at the elevated temperature prior to the BTS measurement. NOTE Mobile charge in dielectric layers above a large area polysilicon or metal-plate cannot be detected, because there is no electric field which drives the ions towards the underlying oxide. To overcome this problem special edge sensitive test structures can be used, that have a large edge/area value, e.g. structures with fingers.
The voltage sweep measurements are done on capacitors. A quasi-static C-V curve is measured and compared with a low-frequency C-V curve. The ionic displacement current, which appears as a peak in the quasi-static C-V curve, is indicative of the mobile ion concentration.
IEC 62417:2010 pdf free download